Corrotech / Products / Coatings / Special coatings / REZORECT™ 125 Ceramic Wearing Compound

REZORECT™ 125 Ceramic Wearing Compound

Product Number

CT125REZ1

CT125REZ10

Product designed for emergency technical repairs, maintenance and protection. A squeegee-applied, highly abrasion-resistant compound designed for maximum performance. Protects surfaces from abrasion and cavitation with specially treated ceramic particles and silicon carbide. Detail description

Hue

light grey

CONSUMPTION CALCULATOR

applied area

m²

layer thickness (DFT)

μm

application losses

practical consumption

liters

Variants

1kg 10kg

Recommended

Detailed description

High abrasion resistant material for spatula application. REZORECT™ 125 CERAMIC WEARING COMPOUND is extremely resistant to abrasion under moderate loads. It protects against abrasion of flowing particles and against abrasion of the surface. Excellent performance in areas subject to abrasion is achieved by specially treated ceramic particles of specific size and silicon carbide, combined with corrosion resistant epoxy resin, which ensures reduced friction and reduced downtime. The product is ideal for repairing the inner rubber lining of containers. Available shades: light grey.

Rezorect's efficient solutions are used in a wide range of industries, both to reduce downtime and maintenance costs. These include the energy, wastewater, oil and gas, petrochemical, pulp and paper, mining, minerals, marine and sustainable energy industries. More about the product at www.rezorect.cz.

Technical data

Manufacturer: Rezorect

Temperature limit in the immersion: 93°C

Temperature limit outside the immersion: 177°C

Recommended thickness of dry coating: 2,000 microns per coat, minimum recommended coats - 2 coats, coating thickness depends on application type and traffic load

Dry matter volume: 100%

Type of activator: modified amine

Mixing ratio: base : activator 4 : 1 (weight ratio)

Available shades: light grey